Glass, which has been made since the time of the Mesopotamians and Egyptians, is little more than a mixture of sand, soda ash and lime. When heated to about 1500 degrees Celsius (℃)this becomes a molten mass that hardens when slowly cooled. The first successful method for making clear, flat glass involved spinning. This method was very effective as the glass had not touched any surfaces between being soft and becoming hard, so it stayed perfectly unblemished, with a 'fire finish'. However, the process took a long time and was labour intensive.

早在美索不达米亚时期和古埃及时期人们就开始制造玻璃,当时制作出的玻璃只不过是沙子、碳酸钠和石灰的混合物而已。该混合物被加热到约1500摄氏度时会变成熔质,慢慢冷却后会硬化。最早成功制出透明、平整的玻璃的工艺中包括旋制法。该制法非常有效,因为玻璃在由软变硬的过程中不会接触任何表面,因此可以一直保持完美无瑕的状态,最后通过“火处理”收尾。然而,该过程耗时很长,而且要耗费大量的劳动力。

Nevertheless, demand for flat glass was very high and glassmakers across the world were looking for a method of making it continuously. The first continuous ribbon process involved squeezing molten glass through two hot rollers, similar to an old mangle. This allowed glass of virtually any thickness to be made non-stop, but the rollers would leave both sides of the glass marked, and these would then need to be ground and polished. This part of the process rubbed away around 20 per cent of the glass, and the machines were very expensive.

尽管如此,人们对平整玻璃的需求很高,全世界的玻璃制造者都在寻找可以连续制造玻璃的方法。第一个连续带式工艺过程是用两个高温滚轴挤压熔化的玻璃——类似老式的轧板机。该工艺可以连续不断地制造几乎各种厚度的玻璃,但是滚轴会在玻璃板的两面都留下痕迹,这就需要对玻璃进行打磨和抛光。这一过程会磨去约20%的玻璃,而且所用的机器也很昂贵。

The float process for making flat glass was invented by Alistair Pilkington. This process allows the manufacture of clear, tinted and coated glass for buildings, and clear and tinted glass for vehicles. Pilkington had been experimenting with improving the melting process, and in 1952 he had the idea of using a bed of molten metal to form the flat glass, eliminating altogether the need for rollers within the float bath. The metal had to melt at a temperature less than the hardening point of glass (about 600~C), but could not boil at a temperature below the temperature of the molten glass (about 1500~C). The best metal for the job was tin.

Alistair Pilkington发明了浮法玻璃制造工艺。该制法可以用来制造用于建筑物上的透明、有色的加膜玻璃,也可以为车辆提供透明的有色玻璃。Pilkington一直在反复实验,研究如何改良熔化工艺。在1952年,他萌生了用熔化金属作基床加工玻璃板的想法,有了这样的金属液槽,就可以彻底淘汰滚轴了。该金属的熔点必须低于玻璃的硬化温度(约600摄氏度),但同时沸点要高于熔化玻璃的温度(约1500摄氏度)。最符合这些条件的金属是锡。

The rest of the concept relied on gravity, which guaranteed that the surface of the molten metal was perfectly flat and horizontal. Consequently, when pouring molten glass onto the molten tin, the underside of the glass would also be perfectly flat. If the glass were kept hot enough, it would flow over the molten tin until the top surface was also flat, horizontal and perfectly parallel to the bottom surface. Once the glass cooled to 604~C or less it was too hard to mark and could be transported out of the cooling zone by rollers~, The glass settled to a thickness of six millimetres because of surface tension interactions between the glass and the tin. By fortunate coincidence, 60 per cent of the flat glass market at that time was for six millimetre glass.

实现这一想法的另一个条件就是重力。重力可以保证熔化金属的表面完全平整且水平。因此,把熔化的玻璃浇在熔锡上时,玻璃的下表面也会完全平整。如果玻璃能够保持足够的高温,它就会在熔锡上慢慢流动,直到其上表面也平整、水平,并与下表面完全平行。一旦将玻璃冷却至604摄氏度或更低,玻璃就会硬化到表面不会被刮花的程度,这样就可以通过滚轴将其运送到冷却槽了。玻璃和锡的表面张力相互作用会使成形的玻璃板的厚度稳定在6毫米。幸运的巧合是,当时市场对玻璃板的需求有60%是6毫米玻璃板。

Pilkington built a pilot plant in 1953 and by 1955 he had convinced his company to build a full-scale plant. However, it took 14 months of non-stop production, costing the company £100, 000 a month, before the plant produced any usable glass. Furthermore, once they succeeded in making marketable flat glass, the machine was turned off for a service to prepare it for years of continuous production. When it started up again it took another four months to get the process right again. They finally succeeded in 1959 and there are now float plants all over the world, with each able to produce around 1000 tons of glass every day, non-stop for around 15 years.

1953年,Pilkington建立了一个试点工厂。到1955年为止,他已经说服他的公司建立成套的工业装置。然而,他们经过14个月的不间断生产且每个月花赞10万英镑,才在厂里首次生产出可用的玻璃。而且,他们在成功生产出能投入市场的玻璃之后,就将机器关闭了,为的是在接下来几年能够持续生产。当机器再次投入生产时,又花了四个月的时间来使生产流程走上正轨。1959年,他们终于成功了。如今浮法制玻工厂遍布全球,每一个工厂都能够15年不间断地日产玻璃千吨。

Float plants today make glass of near optical quality. Several processes - melting, refining, homogenising - take place simultaneously in the 2000 tonnes of molten glass in the furnace. They occur in separate zones in a complex glass flow driven by high temperatures. It adds up to a continuous melting process, lasting as long as 50 hours, that delivers glass smoothly and continuously to the float bath, and from there to a coating zone and finally a heat treatment zone, where stresses formed during cooling are relieved.

今天的浮法制玻工厂可以生产出接近光学质缝的玻璃。在容纳了2000吨熔化玻璃的熔炉内,同时进行着多个程序——熔化、精炼、均质化。这些过程发生在由高温驱动的熔化玻璃流的不同区域,并汇总成为一个长达50小时的无间断熔炼过程,向金属液槽平稳、连续地提供玻璃。接着玻璃会被送往加膜区,最后会被送达热处理区——该区域能够缓释玻璃内部在冷却过程中产生的应力。

The principle of float glass is unchanged since the 1950s. However, the product has changed dramatically, from a single thickness of 6. 8 mm to a range from sub-millimetre to 25 mm, from a ribbon frequently marred by inclusions and bubbles to almost optical perfection. To ensure the highest quality, inspection takes place at every stage. Occasionally, a bubble is not removed during refining, a sand grain refuses to melt, a tremor in the tin puts ripples into the glass ribbon. Automated on-line inspection does two things. Firstly, it reveals process faults upstream that can be corrected. Inspection technology allows more than 100 million measurements a second to be made across the ribbon, locating flaws the unaided eye would be unable to see. Secondly, it enables computers downstream to steer cutters around flaws.

自20世纪50年代以来,浮法制玻的原理不曾改变过。然而,玻璃制品却经历了巨大变化:从之前单一的6.8毫米玻璃板到如今的亚毫米级至25毫米区间任意厚度的玻璃板;从之前很容易被内含物和气泡损毁的玻璃带到如今接近光学完美的玻璃。为了保证最高质量,每一个生产阶段都有监察。偶尔,在精炼过程中也会有一个气泡未被排出,一颗沙粒没有熔化,或是液锡的波动导致玻璃带产生波纹等情况。自动的在线监察有两项任务:一是向上游(生产前阶段)报告生产过程中可以修正的纰漏。监察技术可以在玻璃带上实现每秒超过一亿次的测量,以定位肉眼无法辨认的瑕疵;二是让下游(生产后阶段)计算机操控刀具切割掉有瑕疵的部分。

Float glass is sold by the square metre, and at the final stage computers translate customer requirements into patterns of cuts designed to minimise waste.

浮法玻璃是按平方米出售的。在生产的最后阶段,计算机会根据顾客的需求设计玻璃的裁割方案,以实现浪费的最小化。

Do the following statements agree with the information given in Reading Passage 1?
In boxes 9-13 on your answer sheet, write

9 The metal used in the float process had to have specific properties.

  •  TRUE
  •  FALSE
  •  NOT GIVEN
显示答案
正确答案:TRUE

10 Pilkington invested some of his own money in his float plant.

  •  TRUE
  •  FALSE
  •  NOT GIVEN
显示答案
正确答案:NOT GIVEN

11 Pilkington's first full-scale plant was an instant commercial success.

  •  TRUE
  •  FALSE
  •  NOT GIVEN
显示答案
正确答案:FALSE

12 The process invented by Pilkington has now been improved.

  •  TRUE
  •  FALSE
  •  NOT GIVEN
显示答案
正确答案:TRUE

13 Computers are better than humans at detecting faults in glass.

  •  TRUE
  •  FALSE
  •  NOT GIVEN
显示答案
正确答案:TRUE

考生贡献解析

点击查看题目解析

method第一段第 4行由题目可知,本题需填入一种 method 的名 称。可通过 method 一词定位至文章第 1 段第 3 行。通过 The first successful method for making clear, flat glass involved spinning 可知本题答案 为 spinning。

当前解析由FHC提供

glass , remained第一段倒 数第 2 行由题目可知,本题需填入形容玻璃的形容 词。可沿上道题目的答案按照逻辑关系继 续向后寻找。答案所在句为 ...so it stayed perfectly unblemished。本题答案为 (perfectly) unblemished。

当前解析由FHC提供

disadvantages, slow第一段最 后1句由题目中的 disadvantages 找到文章中表示意思 与上文相反或相对的强转折词 However。同时 根据 slow 判断本题需填入与之并列的形容词。 通过第一段最后一句可确定本题答案为 labour- intensive。

当前解析由FHC提供

ribbon, varying第二段第 4行根据 ribbon 定位至文章第二段第 2 行,根据 non-stop 可知答案应出现在文章第二段第 4 行 之前。再由题目可判断本题需填入一抽象名词, 与 of 构成短语相当于一个形容词。通过原文 This allowed glass of virtually any thickness to be made non-stop 可知本题答案为 thickness,其中 句中的 any 与题目中的 varying 是同义替换。

当前解析由FHC提供

disadvantages, 20%第二段倒 数第 2 行由题目可判断本题需填入一个形容词,且答案 应出现在第二段最后 1 行的 20% 之前。按照逻 辑关系找到修饰 glass 的形容词即可。本题答案 为 marked。

当前解析由FHC提供

第四段第 2行由图可知本题需填入进入 melting zone 的指代某种液体的名词。 由原文 when pouring molten glass onto the molten tin 可知本题 答案为 molten glass。

当前解析由FHC提供

第四段第 3行由图可知本题需填入题目 6 所指代液体进入的区域名称。通过 解答上一题很容易可以判断出本题答案为 molten tin/metal。

当前解析由FHC提供

第四段第 3行由图可知本题需填入题目 6 所指代液体进入的区域名称。通过 解答上一题很容易可以判断出本题答案为 molten tin/metal。

当前解析由FHC提供

metal, float processspecific properties第三段倒数 第2句TRUE 因为上一道题的题型 diagram 和 本 类 题 型 TRUE/ FALSE/NOT GIVEN 都 是 按 照 文章顺序出题,本题可沿上道题 的答案继续寻找。题目中 specific properties 是文章中第三段倒数第 2 句内容的抽象概括。

当前解析由FHC提供

Pilkington, planthis own money第五段第 1 句NOT GIVEN 通过题目中的人 名和 plant 一词定位至文章第五段 第 1 句,但句子中并未出现与 his own money 相关信息,因此无法判 定题目表述是否正确。

当前解析由FHC提供

Pilkington’s first full- scale plantinstant commercial success第五段最后 一句FALSE 通过题目中的专有名词和 具体名词 plant 定位到文章第五段 第 1 句。由第 2 句句首的强转折 词 However 可知,情况向相反的 方向发生变化。此后的句子则具体 说明成功路上的各种阻碍,在最后 一句中看到最终取得成功的时间 是 1959 年,与题目中表述 instant commercial success 相反。

当前解析由FHC提供

process, nowimproved第六段TRUE 由题目中 now 一词定位至 文章第六段第 1 句,本段的内容是 process improved 的具体表现。所 以题目表述与原文相符,表述正确。

当前解析由FHC提供

computers, humansbetter...at detecting faults第七段倒数 第2行TRUE 当句子中出现比较级时, 可通过进行比较的双方和比较特征 三个方面进行判断。题 目 中 的 computers 对 应 文 章 第七段倒数第 3 行的 inspection technology, 题 目 中 的 humans 对 应文章第七段倒数第 2 行 unaided eye。 由 文 章 本 句 中 的 locating flaws the unaided eye would be unable to see 可知,计算机胜过肉 眼。题目表述与原文相符

当前解析由FHC提供

保存解析
取消
保存成功!

题目讨论

如果对题目有疑问,欢迎来提出你的问题,热心的小伙伴会帮你解答。

  • Q1
  • Q2
  • Q3
  • Q4
  • Q5
  • Q6
  • Q7
  • Q8
  • Q9
  • Q10
  • Q11
  • Q12
  • Q13
用户头像
已经输入0个字
发表
Q1全部讨论

如何高效搞定此篇文章?

Sheet glass manufacture: the float process

马上练习